The dehydration-rehydration process in gmelinite-Na |Na7.27K0.28Ca0.15(H2O)21.85|[Al7.71Si17.24O48]-GME, a natural zeolite that can be described as a parallel stacking of double six rings of tetrahedra in the AABB sequence, was studied by X-ray diffraction data. Its space group is P63/mmc with a = 13.764(1) and c = 10.078(1) Å cell parameters. Single-crystal data collections were performed at room conditions and at increasing temperatures, in a hot nitrogen stream, up to the fragmentation of the crystals, which occurs at a temperature as low as 100 °C, and afterward the crystal was cooled down to room conditions. X-ray powder diffraction data showed that gmelinite-Na transforms into a new structure with an AFI-type topology at about 300 °C. At room conditions, extraframework cations are located in two symmetrically independent positions, both of which are coordinated to either framework O atoms or water molecules. When the mineral is heated to 90 °C, about 40% of H2O is lost, and one cation site splits over two positions, which are three-coordinated to the framework O atoms. The dehydration process is completely reversible over a period of hours. X-ray single-crystal data has highlighted that gmelinite-Na when quenched at 100 K displays remarkable modifications in its extraframework content, resulting in a strong disorder in its extraframework ions. As in the case of heating, the mineral restores its structural features when brought back to room temperature.

You do not have access to this content, please speak to your institutional administrator if you feel you should have access.