The high-temperature behaviour of a feldspar-group mineral, filatovite (with the simplified formula: K(Al,Zn)2(As,Si)2O8), in which the Al:As:Si ratio is close to 2:1:1), was studied by in situ high-temperature single-crystal X-ray diffraction and in situ high-temperature (hot stage) Raman spectroscopy up to 600°C. In the temperature range studied (25–600°С) filatovite does not undergo any phase transition, whereas at 800°C it decomposes to X-ray amorphous phase(s). The evolution of 12 main Raman bands was traced during heating, which indicates a gradual change in the crystal structure. The thermal expansion coefficients of filatovite demonstrate a sharply anisotropic character of thermal expansion: the maximal expansion is close to the a axis (α11 = 17.7(1) × 10–6 °C–1), whereas along the b and c axes the thermal expansion coefficients are close to zero. Such behaviour is typical for minerals with a similar crystal structure topology; it indicates the dominant role of structure geometry in the thermal behaviour of the mineral.

You do not have access to this content, please speak to your institutional administrator if you feel you should have access.