The new minerals cuatrocapaite-(NH4) (IMA2018-083) and cuatrocapaite-(K) (IMA2018-084) are the NH4- and K-dominant members of a series with the general formula (NH4,K)3(NaMg□)(As2O3)6Cl6·16H2O. Both minerals were found at the Torrecillas mine, Iquique Province, Chile, where they occur as secondary alteration phases. Both minerals occur as hexagonal tablets up to ~0.3 mm in diameter. They are transparent, with a vitreous lustre and white streak. For both, the Mohs hardness is ca. 2½, the crystals are somewhat flexible, but not elastic, the fracture is irregular and the cleavage is perfect on {001}. The measured densities are 2.65(2) and 2.76(2) g/cm3 for the NH4- and K-dominant species, respectively. Optically, cuatrocapaite-(NH4) is uniaxial (–) with ω = 1.779(3) and ε = 1.541(3) and cuatrocapaite-(K) is uniaxial (–) with ω = 1.777(3) and ε = 1.539(3) (white light). The minerals are insoluble in acids, but decompose in NaOH(aq). The empirical formulas, determined from electron-microprobe analyses, are (NH4)2.48Na1.66Mg0.87K0.09(As12O18.05)Cl5.88·16.02H2O and K2.68Na1.33Mg0.93(NH4)0.31(As12O18.01)Cl6.16·16.04H2O. The minerals are trigonal, space group Rforumla|${\bar 3}$|m; the cuatrocapaite-(NH4) cell parameters are a = 5.25321(19), c = 46.6882(19) Å, V = 1115.80(9) Å3 and Z = 1; the cuatrocapaite-(K) cell parameters are a = 5.2637(15), c = 46.228(8) Å, V = 1109.2(7) Å3 and Z = 1. The structures, refined for cuatrocapaite-(NH4) to R1 = 1.78% for 544 Io > 2σI reflections, contain four types of layers: (1) a planar neutral As2O3 (arsenite) sheet; (2) an (⁠forumla|${\rm NH}_{\rm 4}^{\vskip -2pt\rm \scale65% +} $|⁠,K+) layer that links adjacent arsenite sheets; (3) a Cl– layer placed on the As side of each arsenite; and (4) a layer containing partially occupied Na, Mg and H2O sites that is flanked on either side by Cl layers. The layer sequence for the type 1, 2 and 3 layers is identical to the Cl–As2O3–K–As2O3–Cl layer sequence in the structures of lucabindiite and gajardoite.

You do not have access to this content, please speak to your institutional administrator if you feel you should have access.