2-line ferrihydrite stored in water at ambient temperatures from 4 to 25°C and at ten different pH values between 2.5 and 12 for up to 10–12 y transformed to both goethite and hematite at all temperatures and pH values except at pH 12 where only goethite was formed. The rate and degree of transformation (20–100%) increased with increasing pH and temperature. The hematite/(hematite+goethite) ratio varied between 0 and ∼0.8, increased with increasing temperature and showed a strong maximum at pH 7–8 which increased from 0.1–0.2 at 4°C to 0.7–0.8 at 25°C. The maximum coincides with the zero point of charge of ferrihydrite where its solubility and, thus, its via-solution transformation rate to goethite are minimal. We assume, therefore, that in this pH-range the (slower) via-solution transformation to hematite can more efficiently compete with that to goethite.