Ordered distribution of Au and Ag in the crystal structure of muthmannite, AuAgTe (sub 2) , a rare telluride from Sacarimb, western Romania

Muthmannite, AuAgTe (sub 2) , a rare gold-silver telluride was discovered in a sample from the historical mineralogical collection of the Naturhistorisches Museum of Vienna. The sample is from the gold-telluride deposit of Sacarimb, Metaliferi Mountains, western Romania. Muthmannite occurs as anhedral grains up to 200 mu m associated with large sylvanite crystals and does not show any inclusions or intergrowths of other minerals. The associated minerals are sylvanite, calaverite, and petzite, whereas the gangue mineral is quartz. Muthmannite is pale bronze in color and shows a gray-black streak. No cleavage was observed, the fracture is uneven, and the Vickers hardness (VHN (sub 15) ) is 186 kg/mm (super 2) . Muthmannite is grayish white in reflected light, with very low bireflectance and pleochroism. When observed near sylvanite it is darker and shows a gray color with a slightly bluish tint. Reflectance percentages for R (sub min) and R (sub max) were found to be 40.1, 40.8 (471.1 nm), 38.3, 38.6 (548.3 nm), 37.9, 38.3 (586.6 nm), and 37.7, 38.1 (652.3 nm), respectively. Muthmannite is monoclinic, space group P2/m, with the following unit-cell parameters: a = 5.124(2), b = 4.419(1), and c = 7.437(2) Aa, beta = 89.96(1) degrees , V = 168.4(4) Aa (super 3) , and Z = 2. Electron microprobe analyses gave the chemical formula Au (sub 0.97) Ag (sub 0.99) Te (sub 2.03) . The calculated density (from the ideal formula) is 11.04 g/cm (super 3) . The crystal structure was solved and refined to R = 5.52%. It is based on the NiAs-type structure, with a distorted hexagonal closes-packed array of Te (super 2-) atoms with Au (super 3+) and Ag (super +) occupying all the octahedral sites. The crystal-chemical relationships with other gold-silver tellurides are outlined.