MgO-clay nanocomposites were prepared from a synthetic smectite-type clay, TS, using three different non-ionic surfactants (Igepal CA-720, Brij 30 and Brij 56) and the resulting clay nanocomposites were impregnated with Ni for the methane reforming reaction with carbon dioxide to synthesis gas. A Ni/TS catalyst was also prepared for comparison. The prepared supports and catalysts were characterized by X-ray diffraction, X-ray fluorescence, thermogravimetric analysis and N2 adsorption/desorption isotherms. The thermal stability, pore structure and the surface area strongly influence the catalytic behavior of the catalysts. The methane conversions (at 700°C for 4 h) were 91, 95 and 97% for Ni/TSIGE, Ni/TSBR30 and Ni/TSBR56, respectively, indicating that the surface properties and the catalytic performance of the resulting solids slightly improved as the polyethylene oxide number of the surfactant increased. A reduced conversion (10%) and a rapid deactivation was observed in the Ni/TS catalyst, attributed to its Na content and low thermal stability, which led to sintering and coke deposition.

You do not have access to this content, please speak to your institutional administrator if you feel you should have access.