Two-line ferrihydrite samples were synthesized following conventional procedure. Detailed characterizations of freeze-dried and untreated samples – prepared from direct inclusion of the fresh precipitates in hydrophilic resin – were made by high resolution transmission electron microscopy to investigate in detail their structural organization and to compare the two types of preparations.

Only highly disordered chain-like aggregates of 2–5 nm diameter size nano-particles were revealed within the untreated samples. Conversely, in freeze-dried samples, domains with different degrees of order were recognized, from poorly ordered 2-line ferrihydrite to 3-line ferrihydrite particle aggregates that revealed lattice fringes. Associated with these aggregates, a goethite phase with a modified crystal morphology was also observed.

These HRTEM observations revealed that freeze-drying techniques induce artifacts by disturbing ferrihydrite aggregates while direct inclusion in hydrophilic resin preserves the primary organization of such poorly ordered phases.

You do not currently have access to this article.