Abstract

The structural behavior of gaudefroyite, Ca8Mn3+6[(BO3)6(CO3)2O6], was determined by using Rietveld refinements based on synchrotron powder X-ray-diffraction data from 25 to 486°C. The structure was also refined at 25°C using synchrotron high-resolution powder X-ray-diffraction (HRPXRD) data that gave the pseudohexagonal unit-cell parameters a 10.60791(2), c 5.88603(1) Å, and V 573.605(2) Å3 at room temperature. The expansion of the gaudefroyite structure is nearly isotropic and is caused mainly by an increase in the Ca1–O3 distance. The volume change from 25° to 486°C is 2.2(2)%. Beyond 486°C, significant changes were observed in the X-ray-diffraction traces; they indicate the formation of a minor second phase that exsolved from the host gaudefroyite.

Abstract

Nous avons déterminé le comportement structural de la gaudefroyite, Ca8Mn3+6[(BO3)6(CO3)2O6], au moyen d’affinements Rietveld de données en diffraction X sur poudre obtenues entre 25 et 486°C avec rayonnement synchrotron. La structure a aussi été affinée à 25°C en utilisant des données de haute résolution obtenues avec rayonnement synchrotron; les paramètres réticulaires de la maille pseudo-hexagonale sont a 10.60791(2), c 5.88603(1) Å, et V 573.605(2) Å3 à température ambiante. L’expansion de la structure est presque isotrope, et résulte surtout de l’augmentation de la distance Ca1–O3. Le changement du volume en allant de 25° à 486°C est 2.2(2)%. Au delà de 486°C, nous observons des changements importants dans le spectre de diffraction X; ils indiquent la formation d’une faible quantité d’une seconde phase, exsolvée de la gaudefroyite hôte.

(Traduit par la Rédaction)

You do not currently have access to this article.