Abstract

A new occurrence of the rare mineral species ordoñezite has been found at the Theodoso Soto tin mine, near Sapioris, Durango, Mexico. The average composition of the samples is (Zn0.98Fe0.02)∑1.00Sb2.00O6; the core of the crystals is slightly richer in Fe than the rim. The mineral is uniaxial (+), with all n greater than 2.30 (ncalc is 2.38 at 589 nm); Dobs 6.66 g/cm3, Dcalc 6.67 g/cm3. It is isostructural with ferrotapiolite, with a 4.668(2), c 9.269(6) Å (from powder-diffraction data), space group P42/mnm, and is twinned on {103}. Its crystal structure, refined to R = 4.1, wR = 4.3% using 163 observed reflections, is fully cation-ordered.

Abstract

Nous décrivons les propriétés d’un nouvel exemple d’ordoñezite, espèce rarissime, à la mine d’étain Theodoso Soto, près de Sapioris, Durango, au Mexique. La composition moyenne des échantillons est (Zn0.98Fe0.02)∑1.00Sb2.00O6; le centre des cristaux est légèrement plus enrichi en fer que la bordure. Il s’agit d’un minéral uniaxe positif dont tous les indices de réfraction dépassent 2.30 (ncalc est 2.38 à 589 nm); Dobs 6.66 g/cm3, Dcalc 6.67 g/cm3. L’ordoñezite possède la même structure que la ferrotapiolite, avec a 4.668(2), c 9.269(6) Å (par affinement des données de diffraction X sur poudre), groupe spatial P42/mnm; elle est maclée sur {103}. Sa structure cristalline, affinée jusqu’à R = 4.1, wR = 4.3% en utilisant 163 réflexions observées, montre que les cations sont complètement ordonnés.

(Traduit par la Rédaction)

You do not currently have access to this article.