The stacking structure of tubular halloysite, which is easily damaged by electron-beam radiation, has been investigated by high-resolution transmission electron microscopy (HRTEM) using a new TEM with a computer-assisted minimal-dose system. The new TEM is equipped with a high-speed beam blanker by which the specimen is beam-irradiated only during image acquisition by the recording media. Using a few images taken by a CCD camera with a short exposure time (0.04 s), TEM operations such as area search and brightness adjustment are completed by the computer-assisted system, which can decrease the electron dose delivered before recording final HRTEM images by a factor of 100. The specimen used was halloysite (7 Å) with a tubular morphology from Eureka, Nevada, U.S.A. HRTEM images were taken with the incident electron beam perpendicular to the tube axis, which is parallel to the Yi-axes of the dioctahedral 1:1 layer of halloysite. Lattice fringes in halloysite were almost extinguished with an electron dose of ~2000 electrons (e)/Å2, and it was almost impossible to record crossed lattice fringes without radiation damage using conventional TEMs. By contrast, HRTEM images of high quality and without damage could be recorded with ~400 e/Å2 in the new TEM system. The stacking structures recorded in such images were generally disordered, but ordered packets with one-layer periodicity were often observed. Among them, a stacking sequence that has never previously been observed in kaolinite was identified.

You do not have access to this content, please speak to your institutional administrator if you feel you should have access.